| Material |
Conductivity
|
Resistivity
|
Reference
|
Notes |
|
(%IACS)
|
(Siemens/m)
|
(Ohm-m)
|
(See Below)
|
|
| Antimonial
Tin Solder |
11.90
|
6.902E+06
|
1.449E-07
|
CSNDT
|
|
| Antimonial Lead, 1% (Quenched and Aged) |
7.88
|
4.570E+06
|
2.188E-07
|
CSNDT
|
|
| Antimony |
4.40
|
2.552E+06
|
3.918E-07
|
CSNDT
|
|
| Antimony |
4.66
|
|
3.700E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Arsenic (alpha-metallic) |
6.63
|
|
2.600E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Babbit, Lead Base |
6.00
|
3.480E+06
|
2.874E-07
|
CSNDT
|
|
| Barium (at 0 C) |
28.74
|
|
6.000E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Beryllium |
38.9 - 43.1
|
2.50E+07--2.256E+07
|
4.00E-08--4.43E-08
|
CSNDT
|
|
| Beryllium |
38-43
|
|
4.000E-08
|
MHASM2
|
|
| |
|
|
|
|
|
| Bismuth alloys |
|
|
|
|
|
| Pure Bismuth (at 0 C) |
1.64
|
|
1.050E-06
|
MHASM2
|
conductivity
converted from resistivity |
| A |
3.34
|
|
5.162E-07
|
MHASM2
|
resistivity
converted from conductivity |
| B |
2.43
|
|
7.095E-07
|
MHASM2
|
resistivity
converted from conductivity |
| C |
4.19
|
|
4.115E-07
|
MHASM2
|
resistivity
converted from conductivity |
| G |
1.75
|
|
9.852E-07
|
MHASM2
|
resistivity
converted from conductivity |
| H |
5.00
|
|
3.448E-07
|
MHASM2
|
resistivity
converted from conductivity |
| T |
4.27
|
|
4.038E-07
|
MHASM2
|
resistivity
converted from conductivity |
| Y |
2.57
|
|
6.709E-07
|
MHASM2
|
resistivity
converted from conductivity |
| Z |
7.77
|
|
2.219E-07
|
MHASM2
|
resistivity
converted from conductivity |
| ZZ |
3.27
|
|
5.272E-07
|
MHASM2
|
resistivity
converted from conductivity |
| |
|
|
|
|
|
| Cadmium |
25.20
|
1.462E+07
|
6.842E-08
|
CSNDT
|
|
| Cadmium |
25.00
|
|
7.300E-08
|
MHASM2
|
|
| Calcium |
48.70
|
2.825E+07
|
3.540E-08
|
CSNDT
|
|
| Calcium |
49.60
|
|
3.160E-08
|
MHASM2
|
|
| Cartridge Brass (Annealed) |
28.00
|
1.624E+07
|
6.158E-08
|
CSNDT
|
|
| Cerium (beta phase) |
2.08
|
|
8.280E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cerium (gamma phase) |
2.32
|
|
7.440E-07
|
MHASM2
|
conductivity
converted from resistivity |
| |
|
|
|
|
|
| Cermets |
|
|
|
|
|
| Cr-Al2O3 |
19.82
|
|
8.700E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Cromium carbide type A (83Cr3C2-15Ni-2W) |
20.53
|
|
8.400E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Cromium carbide type B (88Cr3C2-12Ni) |
24.63
|
|
7.000E-08
|
MHASM2
|
conductivity
converted from resistivity |
| TiB2 |
112.69
|
|
1.530E-08
|
MHASM2
|
conductivity
converted from resistivity |
| ZrB2 |
107.76
|
|
1.600E-08
|
MHASM2
|
conductivity
converted from resistivity |
| ZrB2-B |
75-101
|
|
1.7E-8--2.3E-8
|
MHASM2
|
conductivity
converted from resistivity |
| CrB |
86.21
|
|
2.000E-08
|
MHASM2
|
conductivity
converted from resistivity |
| CrB-Ni |
28-45
|
|
3.8E-8--5.8E-8
|
MHASM2
|
conductivity
converted from resistivity |
| CrB-Cr-Mo |
32-47
|
|
3.7E-8--5.4E-8
|
MHASM2
|
conductivity
converted from resistivity |
| Mo2NiB2 |
24-26
|
|
6.6E-8--7.1E-8
|
MHASM2
|
conductivity
converted from resistivity |
| |
|
|
|
|
|
| Cesium |
8.62
|
4.500E+06
|
2.000E-07
|
MHASM2
|
conductivity
(IACS) converted from resistivity |
| Chromium |
8.80
|
5.104E+06
|
1.959E-07
|
CSNDT
|
|
| Chromium (at 20 C) |
13.00
|
|
1.300E-07
|
MHASM2
|
|
| |
|
|
|
|
|
| Cobalt |
|
|
|
|
|
| Cobalt |
27.60
|
1.601E+07
|
6.247E-08
|
CSNDT
|
|
| Cobalt |
27.60
|
|
5.250E-08
|
MHASM2
|
|
| wear-resistant alloy 1 |
1.83
|
|
9.400E-07
|
MHASM2
|
conductivity
converted from resistivity |
| wear-resistant alloy 6 |
2.05
|
|
8.400E-07
|
MHASM2
|
conductivity
converted from resistivity |
| wear-resistant alloy 12 |
1.96
|
|
8.800E-07
|
MHASM2
|
conductivity
converted from resistivity |
| wear-resistant alloy 6B |
1.89
|
|
9.100E-07
|
MHASM2
|
conductivity
converted from resistivity |
| |
|
|
|
|
|
| Columbium |
13.20
|
7.656E+06
|
1.306E-07
|
CSNDT
|
|
| Constantan |
3.52
|
2.042E+06
|
4.898E-07
|
CSNDT
|
|
| Corrodine Lead |
8.30
|
4.814E+06
|
2.077E-07
|
CSNDT
|
|
| Dysprosium |
1.86
|
|
9.260E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Europium |
1.92
|
|
9.000E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Erbium |
2.00
|
|
8.600E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Gadolinium |
1.32
|
|
1.310E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Gallium (polycrystalline) |
11.46
|
|
1.505E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Gilding Metal (Annealed) |
56.00
|
3.248E+07
|
3.079E-08
|
CSNDT
|
|
| Gold |
73.40
|
4.257E+07
|
2.349E-08
|
CSNDT
|
|
| Gold, Pure |
70.00
|
4.060E+07
|
2.463E-08
|
ECTM
|
|
| Gold |
83.69
|
|
2.060E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Graphite |
0.22
|
1.276E+05
|
7.837E-06
|
CSNDT
|
|
| Hafnium |
4.91
|
|
3.510E-07
|
MHASM2
|
conductivity
converted from resistivity |
| |
|
|
|
|
|
| Indium |
|
|
|
|
|
| 100% In |
24.00
|
|
7.184E-08
|
MHASM2
|
resistivity
converted from conductivity |
| 290 (97In-3Ag) |
23.00
|
|
7.496E-08
|
MHASM2
|
resistivity
converted from conductivity |
| 90In-10Ag |
22.10
|
|
7.801E-08
|
MHASM2
|
resistivity
converted from conductivity |
| 300-302 (80In-15Pb-5Ag) |
13.00
|
|
1.326E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 320-345 (70In-30Pb) |
8.80
|
|
1.959E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 60In-40Pb |
7.00
|
|
2.463E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 244 (52In-48Sn) |
11.70
|
|
1.474E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 50In-50Sn |
11.70
|
|
1.474E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 500In-50Pb |
6.00
|
|
2.874E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 40In-60Pb |
5.20
|
|
3.316E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 25In-75Pb |
4.60
|
|
3.748E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 25In-37.5Pb-37.5Sn |
7.80
|
|
2.210E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 136 (21In-18Pb-12Sn-49Bi) |
2.43
|
|
7.095E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 19In-81Pb |
4.50
|
|
3.831E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 307-323 (12In-18Pb-70Sn) |
12.20
|
|
1.413E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 5In-95Pb |
5.10
|
|
3.381E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 5In-90Pb-5Ag |
5.60
|
|
3.079E-07
|
MHASM2
|
resistivity
converted from conductivity |
| 5In-92.5Pb-2.5Ag |
5.50
|
|
3.135E-07
|
MHASM2
|
resistivity
converted from conductivity |
| |
|
|
|
|
|
| Iridium |
|
|
|
|
|
| Iridium |
36.61
|
|
4.710E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Iridium |
32.60
|
1.891E+07
|
5.289E-08
|
CSNDT
|
|
| Iridium - Platinum Alloys |
9.10
|
5.278E+06
|
1.895E-07
|
CSNDT
|
|
| Iridium - Platinum Alloys,
18% Nickel Silver Alloy B |
5.20
|
3.016E+06
|
3.316E-07
|
CSNDT
|
|
| |
|
|
|
|
|
| Lead |
|
|
|
|
|
| Lead |
8.40
|
4.872E+06
|
2.053E-07
|
ECTM
|
|
| Lead |
8.35
|
|
2.064E-07
|
MHASM2
|
conductivity
converted from resistivity |
| 1% Antimonial (Quenched & Aged) |
7.88
|
4.570E+06
|
2.188E-07
|
CSNDT
|
|
| Corrodine |
8.30
|
4.814E+06
|
2.077E-07
|
CSNDT
|
|
| Hard (Quenched & Aged) |
7.70
|
4.466E+06
|
2.239E-07
|
CSNDT
|
|
| |
|
|
|
|
|
| Lithium |
20.20
|
1.172E+07
|
8.535E-08
|
CSNDT
|
|
| Lithium |
18.44
|
|
9.350E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Manganese (alpha phase) |
0.90
|
|
1.440E-06
|
MHASM2
|
|
| Mercury |
1.80
|
1.044E+06
|
9.579E-07
|
CSNDT
|
|
| Mercury |
1.80
|
|
9.580E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Mischmetal |
2.16
|
|
8.000E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Molybdenum |
33.00
|
1.914E+07
|
5.225E-08
|
CSNDT
|
|
| Molybdenum |
33.00
|
|
5.200E-08
|
MHASM2
|
|
| Monel |
3.60
|
2.088E+06
|
4.789E-07
|
ECTM
|
|
| Monel |
3.58
|
2.076E+06
|
4.816E-07
|
CSNDT
|
|
| Muntz Metal (Annealed) |
28.00
|
1.624E+07
|
6.158E-08
|
CSNDT
|
|
| Neodymium |
2.68
|
|
6.430E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Niobium |
13.20
|
|
1.600E-07
|
MHASM2
|
|
| Osmium |
18.20
|
1.056E+07
|
9.473E-08
|
CSNDT
|
|
| Osmium |
21.23
|
|
8.120E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Palladium |
16.00
|
9.280E+06
|
1.078E-07
|
CSNDT
|
|
| Palladium |
17.36
|
|
9.930E-08
|
MHASM2
|
conductivity
converted from resistivity |
| |
|
|
|
|
|
| Permanent Magnet Materials |
|
|
|
|
|
| 3 1/2 % Cr steel |
5.95
|
|
2.900E-07
|
MHASM2
|
conductivity
converted from resistivity |
| 6% W steel |
5.75
|
|
3.000E-07
|
MHASM2
|
conductivity
converted from resistivity |
| 17% Co steel |
6.16
|
|
2.800E-07
|
MHASM2
|
conductivity
converted from resistivity |
| 36% CO steel |
6.39
|
|
2.700E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 1 |
2.30
|
|
7.500E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 2 |
2.65
|
|
6.500E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 3 |
2.87
|
|
6.000E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 4 |
2.30
|
|
7.500E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 5 |
3.67
|
|
4.700E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 5DG |
3.67
|
|
4.700E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 5-7 |
3.67
|
|
4.700E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 6 |
3.45
|
|
5.000E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 7 |
2.97
|
|
5.800E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 8 |
3.45
|
|
5.000E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cast Alnico 12 |
2.78
|
|
6.200E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Sintered Alnico 2 |
2.54
|
|
6.800E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Sintered Alnico 4 |
2.54
|
|
6.800E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Sintered Alnico 5 |
3.45
|
|
5.000E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Sintered Alnico 6 |
3.25
|
|
5.300E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Bonded ferrite A |
N/A
|
|
1.000E+05
|
MHASM2
|
conductivity
converted from resistivity |
| Sintered ferrite 1 |
N/A
|
|
1.000E+05
|
MHASM2
|
conductivity
converted from resistivity |
| Sintered NdFeB |
1.08
|
|
1.600E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Bonded NdFeB |
N/A
|
|
1.000E+00
|
MHASM2
|
conductivity
converted from resistivity |
| Hot-pressed NdFeB |
1.08
|
|
1.600E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Hot-formed ndFeB |
1.08
|
|
1.600E-06
|
MHASM2
|
conductivity
converted from resistivity |
| cunife |
9.58
|
|
1.800E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Platinum cobalt |
6.16
|
|
2.800E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Cobalt rare earth |
3.45
|
|
5.000E-07
|
MHASM2
|
conductivity
converted from resistivity |
| |
|
|
|
|
|
| Platinum |
|
|
|
|
|
| Platinum |
16.28
|
9.442E+06
|
1.059E-07
|
CSNDT
|
|
| Platinum |
17.50
|
|
9.850E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Commercial |
11.60
|
6.728E+06
|
1.486E-07
|
CSNDT
|
|
| Platinum - Iridium Alloys |
9.10
|
5.278E+06
|
1.895E-07
|
CSNDT
|
|
| Platinum - Iridium Alloys, 18% Nickel Silver Alloy B |
5.20
|
3.016E+06
|
3.316E-07
|
CSNDT
|
|
| Platinum - Nickel Alloys |
7.40
|
4.292E+06
|
2.330E-07
|
CSNDT
|
|
| Platinum - Nickel Alloys |
13.60
|
7.888E+06
|
1.268E-07
|
CSNDT
|
|
| Ruthenium (Contact Grade) |
4.00
|
2.320E+06
|
4.310E-07
|
CSNDT
|
|
| Ruthenium (Jewelry Grade) |
5.50
|
3.190E+06
|
3.135E-07
|
CSNDT
|
|
| |
|
|
|
|
|
| Potassium |
23.95
|
|
7.200E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Praseodymium |
2.46
|
|
7.000E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Promethium |
2.30
|
|
7.500E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Rhenium |
9.30
|
|
1.854E-07
|
MHASM2
|
resistivity
converted from conductivity |
| Ruthenium |
22.70
|
1.317E+07
|
7.595E-08
|
CSNDT
|
|
| Ruthenium |
25.35
|
|
6.800E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Ruthenium - Platinum (Contact Grade) |
4.00
|
2.320E+06
|
4.310E-07
|
CSNDT
|
|
| Ruthenium - Platinum (Jewelry Grade) |
5.50
|
3.190E+06
|
3.135E-07
|
CSNDT
|
|
| Scandium |
3.07
|
|
5.620E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Selenium |
14.40
|
8.352E+06
|
1.197E-07
|
CSNDT
|
|
| |
|
|
|
|
|
| Silver |
|
|
|
|
|
| Pure |
105.00
|
6.090E+07
|
1.642E-08
|
ECTM
|
|
| Pure |
108.40
|
6.287E+07
|
1.591E-08
|
CSNDT
|
|
| 18% Nickel Alloy A |
6.00
|
3.480E+06
|
2.874E-07
|
CSNDT
|
|
| |
|
|
|
|
|
| Sodium |
39.82
|
|
4.330E-08
|
MHASM2
|
conductivity
converted from resistivity |
| |
|
|
|
|
|
| Solder |
|
|
|
|
|
| Antimonial Tin |
11.90
|
6.902E+06
|
1.449E-07
|
CSNDT
|
|
| Tin Silver |
16.60
|
9.628E+06
|
1.039E-07
|
CSNDT
|
|
| 20-80 Soft |
9.80
|
5.684E+06
|
1.759E-07
|
CSNDT
|
|
| 5-95 Soft |
8.80
|
5.104E+06
|
1.959E-07
|
CSNDT
|
|
| 50-50 Soft |
11.00
|
6.380E+06
|
1.567E-07
|
CSNDT
|
|
| |
|
|
|
|
|
| Tantalum |
13.90
|
8.062E+06
|
1.240E-07
|
CSNDT
|
|
| Tantalum |
13.00
|
|
1.350E-07
|
MHASM2
|
|
| Technetium |
9.32
|
|
1.850E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Terbium |
1.50
|
|
1.150E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Thallium (at 0 C) |
11.49
|
|
1.500E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Thorium |
11.00
|
|
1.570E-07
|
MHASM2
|
|
| Thulium |
2.55
|
|
6.760E-07
|
MHASM2
|
conductivity
converted from resistivity |
| |
|
|
|
|
|
| Tin |
|
|
|
|
|
| Pure |
15.00
|
8.700E+06
|
1.149E-07
|
CSNDT
|
|
| Solder (Antimonial) |
11.90
|
6.902E+06
|
1.449E-07
|
CSNDT
|
|
| Foil |
4.20
|
2.436E+06
|
4.105E-07
|
CSNDT
|
|
| Bronze |
14.00
|
8.120E+06
|
1.232E-07
|
CSNDT
|
|
| Silver Solder |
16.60
|
9.628E+06
|
1.039E-07
|
CSNDT
|
|
| |
|
|
|
|
|
| Tungsten |
31.40
|
1.821E+07
|
5.491E-08
|
CSNDT
|
|
| Tungsten |
30.00
|
|
5.300E-07
|
MHASM2
|
|
| Uranium |
6.00
|
3.480E+06
|
2.874E-07
|
CSNDT
|
|
| Vanadium |
6.60
|
3.828E+06
|
2.612E-07
|
CSNDT
|
|
| Waspaloy |
1.40
|
8.120E+05
|
1.232E-06
|
ECTM
|
|
| White Metal |
11.10
|
6.438E+06
|
1.553E-07
|
CSNDT
|
|
| Ytterbium |
6.90
|
|
2.500E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Yttrium |
2.89
|
|
5.960E-07
|
MHASM2
|
conductivity
converted from resistivity |
| |
|
|
|
|
|
| Zinc |
|
|
|
|
|
| Commercial Rolled |
28.00
|
1.624E+07
|
6.158E-08
|
CSNDT
|
|
| Die Cast |
25.00
|
1.450E+07
|
6.897E-08
|
CSNDT
|
|
| Die Cast |
27.00
|
1.566E+07
|
6.386E-08
|
CSNDT
|
|
| AG40A |
27.00
|
|
6.400E-08
|
MHASM2
|
|
| AC43A |
27.00
|
|
6.386E-08
|
MHASM2
|
resistivity
converted from conductivity |
| ZA-8 |
27.70
|
|
6.224E-08
|
MHASM2
|
resistivity
converted from conductivity |
| ZA-12 |
28.30
|
|
6.100E-08
|
MHASM2
|
|
| ZA-27 |
29.70
|
|
5.800E-08
|
MHASM2
|
|
| ILZRO 16 |
20.53
|
|
8.400E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Commercial Rolled Zinc (Zn-0.08Pb) |
28.40
|
|
6.200E-08
|
MHASM2
|
|
| Commercial Rolled Zinc (Zn-0.3Pb-0.03Cd) |
32.00
|
|
6.060E-08
|
MHASM2
|
|
| Commercial Rolled Zinc (Zn-0.06Pb-0.06Cd) |
32.00
|
|
6.060E-08
|
MHASM2
|
|
| Copper-Hardened Rolled Zinc (Zn-1.0Cu) |
28.00
|
|
6.200E-08
|
MHASM2
|
|
| Rolled Zinc Alloy (Zn-1.0Cu-0.010Mg) |
27.00
|
|
6.300E-08
|
MHASM2
|
|
| Zn-Cu-Ti Alloy (Zn-0.8Cu-0.15Ti) |
27.00
|
|
6.240E-08
|
MHASM2
|
|
| Superplastic Zinc (Zn-22Al) (annealed) |
32.00
|
|
6.000E-08
|
MHASM2
|
|
| |
|
|
|
|
|
| Zirconium |
|
|
|
|
|
| Zirconium |
4.20
|
2.436E+06
|
4.105E-07
|
CSNDT
|
|
| Zirconium |
3.40
|
1.972E+06
|
5.071E-07
|
ECTM
|
|
| Reactor grade and grade 702 |
4.34
|
|
3.970E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Zr-2.5Nb, grade 705, and grade 706 |
3.13
|
|
5.500E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Zircaloy - 2 |
2.40
|
1.392E+06
|
7.184E-07
|
ECTM
|
|
| Zircaloy-2, Zircaloy-4, and grade704 |
2.33
|
|
7.400E-07
|
MHASM2
|
conductivity
converted from resistivity |
|
|
|
|
|
|