| Material |
Conductivity
|
Resistivity
|
Reference
|
Notes |
|
(% IACS)
|
(Siemens/m)
|
(Ohm-m)
|
(See Below)
|
|
| Nickel
Alloys |
|
|
|
|
|
| Nickel 200 |
18.15
|
|
9.500E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Nickel 201 |
20.28
|
|
8.500E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Nickel 205 |
18.15
|
|
9.500E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Nickel 211 |
10.20
|
|
1.690E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Nickel 212 |
15.82
|
|
1.090E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Nickel 222 |
19.59
|
|
8.800E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Nickel 270 |
22.99
|
|
7.500E-08
|
MHASM2
|
conductivity
converted from resistivity |
| Duranickel 301 (precipitation hardened) |
4.07
|
|
4.240E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 400 |
3.15
|
|
5.470E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 401 |
3.53
|
|
4.890E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy R-405 |
3.38
|
|
5.100E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 450 |
4.18
|
|
4.120E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy K-500 (precipitation hardened) |
2.80
|
|
6.150E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 230 |
1.38
|
|
1.250E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 600 |
1.67
|
|
1.030E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 601 |
1.45
|
|
1.190E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 617 (solution annealed) |
1.41
|
|
1.220E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 625 |
1.34
|
|
1.290E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 690 |
1.50
|
|
1.148E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 718 (precipitation hardened) |
1.38
|
|
1.250E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy X750 |
1.41
|
|
1.220E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 751 |
1.41
|
|
1.220E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy C-276 |
1.33
|
|
1.300E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy HX (solution annealed) |
1.49
|
|
1.160E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy S (solution annealed) |
1.35
|
|
1.280E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy X |
1.46
|
|
1.180E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 556 |
1.81
|
|
9.520E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 800 |
1.74
|
|
9.890E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 825 |
1.53
|
|
1.130E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 925 |
1.48
|
|
1.166E-06
|
MHASM2
|
conductivity
converted from resistivity |
| 20Cb3 |
1.59
|
|
1.082E-06
|
MHASM2
|
conductivity
converted from resistivity |
| 20Mo-4 |
1.63
|
|
1.056E-06
|
MHASM2
|
conductivity
converted from resistivity |
| 20Mo-6 |
1.59
|
|
1.082E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 902 (precipitation hardened) |
1.69
|
|
1.020E-06
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 903 (precipitation hardened) |
2.83
|
|
6.100E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 907 (precipitation hardened) |
2.47
|
|
6.970E-07
|
MHASM2
|
conductivity
converted from resistivity |
| Alloy 909 (precipitation hardened) |
2.37
|
|
7.280E-07
|
MHASM2
|
conductivity
converted from resistivity |
| 18% Nickel Sil |
6.00
|
3.480E+06
|
2.874E-07
|
CSNDT
|
|
|
|
|
|
|
|